• ER2319（AlCu6MnZrTi） aluminum/magnesium GMAW (MIG) welding alloy

• Designed for welding heat treatable base alloys, specifically 2XXX series alloys

• Lower melting point and more fluidity than 2XXX series filler alloys

• Low sensitivity to weld cracking with 2XXX series base alloys

• ER2319 weld metal can serve from -270°C up to 300°C for continuous service

• All position, except vertical down welding

• Gray (post anodized) color

AWS A5.10 ER2319（AlCu6MnZrTi）aluminum welding wire.pdf

• Liquidus 1171°F (643°C) (as welded 2219/2XXX base plate)

• Tensile Strength 290 - 340Mpa (as welded 2219/2XXX base plate)

• Yield Strength 170 - 220Mpa (as welded 2219/2XXX base plate)

• Density 2.65g/mm3  (as welded 2219/2XXX base plate)

• Elongation (A) 8 - 14% (as welded 2219/2XXX base plate)

AWS A5.10 ER2319 aluminum welding wire is mainly used to weld 2219 aluminum alloy, other 2xxx series Al-Cu alloys and some cast aluminum alloys for high strength structural applications.

• ER2319 Aluminium MIG Welding Wire

• Choose Your MIG Wire Size in mm: 0.8mm / 0.9mm / 1.0mm / 1.2mm/ 1.6mm/ 2.0mm

• Choose Your MIG Wire Size in inch: 0.030 / 0.035 / 0.040 / 0.045/ 0.063/ 0.079 / 3/16 - 3/64

• Choose Your Wire Spool Weight(Package): 0.5kg / 2kg / 7kg

• Choose Your TIG Wire Size:  1.2mm/ 1.6mm/ 2.0mm/ 2.4mm/ 3.2mm/ 4.0mm/ 5.0mm

• Choose Your Wire tube Weight(Package): 2kg / 5kg / 10kg / 1LB / 2LB / 4.5LB / 15.5LB / 20LB

• gasless aluminum welding wire Winding Requirements

  Filler metal on spools and in coils without support shall be wound so that kinks, waves, sharp bends, overlapping,  wedging are not encountered, leaving the filler metal free to unwind without restriction. The outside end of the filler metal (the end with which welding is to begin) shall be identified so it can be located readily and shall be fastened to avoid unwinding.

  The outermost layer of spooled electrode or spooled rod shall not be closer than 1/8 in. [3 mm] to the outside diameter of the flanges.

  The cast and helix of filler metal on spools shall be such that the filler metal will feed in an uninterrupted manner in automatic and semiautomatic equipment.

  
  

• aluminum flux cored welding wire Filler Metal Identification

  Mig welding with aluminum wire The product information and the precautionary information required in Section 20, Marking of Packages, shall also appear on each coil and spool.

  030 aluminum welding wire,Coils without support shall have a tag containing this information securely attached to the filler metal at the inside end of the coil.

  Spools shall have the information securely affixed in a prominent location on the outside of at least one flange of the spool.

•  flux core aluminum welding wire Packaging

  Filler metal shall be suitably packaged to ensure against damage during shipment and storage under normal conditions.

  The following product information (as a minimum of low temperature aluminum welding wire) 

  shall be legibly marked so as to be visible from the outside of each unit package: 

  (1) AWS specification and classification designation (year of issue may be excluded best wire for welding aluminum) 

  (2) Supplier's name and trade designation 

  (3) Size and net weight 

  (4) Lot, control, or heat number

• Protect yourself and others. Read and understand this label of aluminum alloy welding wire. FUMES and GASES can be hazardous to your health.ARC RAYS can injure eyes and burn skin. aluminum mig welding wire ELECTRIC SHOCK can KILL. 

• aluminum mig welding wire speed and voltage chart,Before use, read and understand the manufacturer's instructions, Material Safety Data Sheets (MSDSs), and your employer's safety practices. 

• aluminum welding wire types have too many kinds ,Keep your head out of the fumes.Use enough ventilation, exhaust at the arc, or both, to keep fumes and gases away from your breathing zone and the general area.Wear correct eye, ear, and body protection. 

• welding aluminum with wire feed welder,Do not touch live electrical parts.See American National Standard, ANSI 249.1, Safety in Welding, Cutting, and Allied.

ER2319 mig welding aluminium wire 10 famous brand are which factory?

1:sanzhong, 2:giant, 3:safra, 4:Hobart, 5:SAF, 6:ALCOTEC, 7:INDALCO, 8:GULF, 9:Oxford, 10:harris

ER2319 aluminum mig wire supplier and factories or wholesale locates in such countries like?

China,America,Brazil,England,Russia,Poland,India,Pakistan,NewZealand,Korea,Australia,Dubai,Turkey,Indonesia,UAE.

aluminium bronze welding wire can filler feed how many welders?1060,1070,1080,1350,1100,2014,2036,2219,3003,ALCLAD3003,3004,ALCLAD3004,5005,5050,5052,5652,5083,5456,5086,5056,

511.0,512.0,513.0,514.0,5154,5254,535.0,5454,6005,6063,,6101,6151,6201,6351,6951,6061,6070,7005,7021,7039,7046,710.0,

711.0,7146,413.0,443.0,444.0,356.0,A356.0,A357.0,359.0,319.0,333.0,354.0,355.0,C355.0,380.0

Similiar aluminium welding wire to AWS A5.10 ER2319（AlCu6MnZrTi）aluminum welding wire?

ER4145 Aluminum Welding Wire, AWS A5.10, AlSi10Cu4 alloy filler metal for 2xxx heat treatable aluminum alloys.

ER3103 Aluminum Welding Wire, AWS A5.10, AlMn1 alloy for welding 3003 / 3103 aluminum manganese alloy.

Model ER2117 Aluminum Welding Wire, custom alloy grade, NOT AWS A5.10 classification.

Model ER7075 Aluminum Welding Wire, custom high strength Al-Zn-Mg-Cu filler metal, no AWS A5.10 designation.

Model ER7055 Aluminum Welding Wire, custom ultra-high strength aluminum filler metal, no AWS A5.10 designation.

ER2024: Al-Cu-Mg type; higher magnesium, easier hot cracking

AWS A5.10 ER2319（AlCu6MnZrTi）aluminum welding wire VS ER3103?

ER2319 and ER3103 are both AWS A5.10 solid aluminium MIG/TIG wires, but they are designed for completely different applications. ER2319 is a heat-treatable Al-Cu filler metal with copper, zirconium and titanium; it delivers high strength after T6 post-weld heat treatment and is mainly used for welding 2219 and other 2xxx high-strength aluminium alloys. ER3103 is non-heat-treatable Al-Mn filler metal with outstanding ductility and corrosion resistance, used for joining 3xxx aluminium-manganese alloys such as 3003 and 3103. They cannot substitute each other due to huge differences in alloy system and mechanical performance.

AWS A5.10 ER2319（AlCu6MnZrTi）aluminum welding wire VS ER4145?

ER2319 and ER4145 are both AWS A5.10 solid aluminium MIG/TIG wires using pure argon shielding gas. ER2319 is heat-treatable Al-Cu filler metal with Zr and Ti grain refiners, developed for welding 2219 high-strength aluminium alloy and achieving high mechanical properties after T6 post-weld heat treatment. ER4145 is Al-Si-Cu filler with excellent weld pool fluidity and hot cracking resistance, mainly used for repairing aluminium castings. It cannot be hardened by heat treatment and cannot substitute ER2319 for critical high-strength structural welds.

How to choose a suitable gasless mig aluminium welding wire?or what type of filler wire is best for tig welding for aluminium?

General Notes:

1.Service conditions such as immersion in fresh or salt water,exposure to specific chemicals,or asustained high temperature,aluminium welding wire for high heat(over 150F [66℃)may limit the choice of filler metals welding wire aluminium, aluminium welding wire for mig Filler metals ER5183,ER5356 welding rod,ER5556 are not recommended for sustained elevated temperature service.

2.aluminium mig welding wire recommendations in this table apply to gas shielded arc welding processes.For oxyfuel gas welding,only ER1188,ER1100,ER4043,ER4047,ER4145 filler metals are ordinarily used and aluminium welding wire specification.

3.Where no filler metal is listed,aluminum alloy welding wire ,the base metal combination is not recommended for welding

 aluminium welding wire gasless.

Notes:

a. ER4145 may be used for some applications to some aluminum alloy welding wire.

b. ER4047 may be used for some applications to some flux cored aluminium welding wire.

c. ER4043 may be used for some applications to some aluminium magnesium welding wire.

d. ER5183,ER5356,or ER5556 may be used to some aluminium welding wire grades.

e. ER2319 may be used for some applications.It can supply high strength when the weldment is postweld solution heat treated and aged.

f. alum.welding wire ER5183,ER5356,ER5554,ER5556,and ER5654 may be used In some cases:(1)   improved color match afer anodizing treatment,(2) highest weld ductility (3) higher weld strength.ER5554 is suitable for sustained elevated temperature service.

g. alum welding wire ER4643 will provide higher strength in 1/2 in.[12mm]and thicker groove welds in 6XXX  base alloys when postweld solution heat treated and aged.

h. flux core aluminum wire Filler metal with the same analysis as the base metal is sometimes used.The following wrought filler metals possess the same chemical composition limits as cast filler alloys: ER4009 and r4009 as R-C355.0;ER4010 and R4010 as R-A356.0; R4011 as R-A357.0.

i. Mig welding aluminum wire ,Base metal alloys 5254 and 5652 are used for hydrogen peroxide service.ER5654 filler metal is used for welding both alloys for service temperatures below 150F [66°℃].

j. ER1100 may be used for some applications in wire feed welding aluminum.